Grade 316/316L (1.4401/1.4401) stainless steel is the second most common used commercial grade of stainless steel. Cut to length round bar, Cut to size plate, Cut to size sheet, 1.4401, 1.4404, 316/316L, Grade 316, Grade 316L, AISI 316, AIAI 316L
ASTM A240 316L (S31603) stainless steel plate. ASTM A240 standard specification for chromium and chromium-nickel stainless steel plate, sheet, and strip for pressure vessels and for general applications. Supplementary Technology:HIC Test NACE MR0175 Z15 Z25 Z35 S1 S2Gangsteel is specialized in supplyingASTM A240 steel plate inA240 316L. Our Alloy 316H Stainless Steel Plate - Sandmeyer SteelGeneral Properties. Alloy 316H (UNS S31609) is a high carbon modification of Alloy 316 developed for use in elevated temperature service. The alloy has higher strength at elevated temperatures and is used for structural and pressure vessel
General Properties. Alloy 316H (UNS S31609) is a high carbon modification of Alloy 316 developed for use in elevated temperature service. The alloy has higher strength at elevated temperatures and is used for structural and pressure vessel Comparison Table of Stainless Steel GradesComparison Table of Stainless Steel Grades. Stainless steel is also called as stainless acid resistant steel. It is very good corrosion resistant, aesthetically beautiful, non-fade and easy to clean. Moreover, its life time is very long. Stainless steel castings are widely used in the auto parts, home appliances and building industries, etc.
Since pricing and corrosion resistance are both equally important when deciding a grade for a particular selection. In case of Duplex and Stainless Steel 316, there is no clear winner. Metline Industries supplies high quality Duplex stainless steel 2205 rods and bars, as well as Stainless Steel 316L stainless steel bars and rods. Both grades EN 1.4404 / AISI 316L - *AISI 316L - AcerinoxGrades C Si Mn P S Cr Ni Mo Ti Cu Other; ACX 240 =0.030 =0.75 =2.00 =0.040 =0.030:16.00-18.00:10.00-12.00:2.00-2.50---ACX 332 =0.030 =0.75 =2.00 =0.040 =0.030:16
astm:en:uns:others:a351 cn7m:1.4527--a351:1.4593:j93254:254 smo:ck3mcun:1.4469:s32654:654 smo SS904L AISI 904L Stainless Steel (UNS N08904) Material ASTM SAE AISI 904L Stainless Steel (UNS N08904) AISI 904L stainless steel (UNS N08904) is a high alloy austenitic stainless steel. Compared with 316L, SS904L has lower carbon (C) content, higher chromium (Cr) content, and approximatively twice the nickel (Ni) and molybdenum (Mo) content of 316L, which makes it have higher high temperature oxidation resistance,
56 rows · Stainless Steel Pipes - Comparing of American and European Standards - Stainless Steel EN 1.4435 AISI 316L X2CrNiMo18-14-3 UNS Description :1.4435 / AISI 316 L is an austenitic chromium-nickel-molybdenum stainless steel with low carbon content. Special properties :1.4435 is a higher alloyed variant of 1.4404 and is used as a medical grade due to its excellent resistance of all corrosions.
Steel Grade Equivalent Table (EN, SAE/AISI, UNS, DIN, BS, UNI, JIS) The table below compares common grades of materials from various international specifications. Note that materials compared are the nearest available grade and Table of Steel Equivalent Grades (EN, SAE/AISI, UNS, DIN Jul 24, 2010 · Table of Steel Equivalent Grades (EN, SAE/AISI, UNS, DIN, BS, UNI, JIS) The table below compares steel equivalent grades of materials from various international specifications. Note that materials compared are the nearest available grade and may have slight variations in actual chemistry.
Although it can have a higher carbon content, there seems to be no mechanical property advantage to 316Ti since there is no difference in minimum yield stress for the three variations 316/1.4401, 316L/1.4404, 316Ti/1.4571 in any of the basic EN standards, EN 10088-2 (General application), EN 10088-4 (Structural application) and 10028-7 (Pressure vessel application). Why? Why? Why? 316Ti UNS S31635 - Rolled Alloys, Inc.In all three Euronorms, the Rp0.2 (YS) is listed as minimum 220 MPa (32 KSI) for plate. In ASTM standards there is a slightly lower YS for 316L (25 KSI) versus 316 and 316Ti (30 KSI), but since nearly all 316L is dual certified as 316, there is no practical difference.
There are 122 equivalent materials for AISI 316L Stainless Steel. See the equivalents for ASTM, DIN, AFNOR, BS, UNI, SS, SAE, JIS, EN, GOST, GB, UNS, UNE and AISI.